当前位置:首页 > 产品中心 > 工程塑料 > PA6 系列 >
牌号Grade
特征Feature
PA6001
环保阻燃(V-0,0.8 mm),优异的表面性能
FR(V-0,0.8 mm), Outstanding surface
PA6002
30%玻纤增强,环保阻燃(V-0,0.8 mm),高强度,高耐温,850℃灼热丝不起燃
30%GF reinforced, FR(V-0,0.8 mm), High strength, High heat resistance, No fire GWT(850℃)    
PA6003
无卤阻燃(V-0,0.8 mm),快速结晶
No-halogen FR(V-0,0.8 mm), Fast crystallization
PA6004
30%玻纤增强,无卤阻燃(V-0,0.8 mm),快速结晶
30%GF reinforced, No-halogen FR(V-0,0.8 mm)
PA6005
超韧,优异的耐低温性能
Excellent impact, Excellent low temperature resistance
PA6006
20%玻纤增强,耐冲击
20%GF reinforced, Good impact
PA6007
30%玻纤增强,良好的尺寸稳定性,高机械性能
30%GF reinforced, Good size stability, High mechanical properties
PA6008
30%玻纤增强,良好的尺寸稳定性,高机械性能,优异的耐磨性能
30%GF reinforced, Good size stability, High mechanical properties,Excellent wear resistance  
PA6009
50%玻纤增强,低浮纤,良好的尺寸稳定性,高耐温
50%GF reinforced, Excellent surface, Good size stability, High heat resistance 

 
性能参数
Performance parameters

 

性能
Properties
测试标准
TestMethod
测试条件
TestCondition
单位
Unit
001
002
003
004
005
006
007
008
009
物理性能
Physical
比重
SpecificGravity
ASTMD792
23℃
g/cm3
1.25
±0.05
1.52
±0.05
1.15
±0.05
1.52
±0.05
1.05
±0.05
1.30
±0.05
1.35
±0.05
1.38
±0.05
1.55
±0.05
熔融指数
MeltFlowIndex
ASTMD1238
235℃,2.16kg
g/10min
20
25
30
25
20
25
25
25
20
模塑收缩率
MoldShrink,Linear-Flow
ASTMD955
3.2mm
%
1.1~1.6
0.4~0.9
1.1~1.6
0.4~0.9
1.4~1.8
0.5~0.9
0.4~0.9
0.4~0.9
0.2~0.6
吸水率
WaterAsorption
ASTMD570
24hrs,23℃
%
1.2
0.8
0.9
0.8
1.2
0.8
0.8
0.8
0.7
机械性能Mechanical
拉伸强度
TensileStrength
ASTMD638
10mm/min
MPa
60
145
60
135
45
130
155
140
195
断裂伸长率ElongationatBreak
ASTMD638
10mm/min
%
15
2.1
15
2
50
25
4
3
3.5
弯曲强度
FlexuralStrength
ASTMD790
2mm/min
MPa
85
210
85
190
63
150
230
210
295
弯曲模量FlexuralModulus
ASTMD790
2mm/min
MPa
2500
8500
2500
8500
1700
4000
7800
7300
13000
IZOD缺口冲击强度
IZODNotchedImpactStrength
ASTMD256
3.2mm,23℃
J/m
100
115
100
110
750
350
185
110
230
热性能Thermal
热变形温度
HeatDistortionTemperature
ASTMD648
1.8MPa,3.2mm
65
215
75
215
60
210
213
210
215
0.45MPa,3.2mm
190
220
190
220
205
215
220
215
220
可燃性Flammablity
阻燃等级
FlameRating
UL94
3.2mm
Class
V0
V0
V0
V0
HB
HB
HB
HB
HB
1.6mm
Class
V0
V0
V0
V0
HB
HB
HB
HB
HB
加工工艺Processing
加工温度范围
MeltTemp.Range
 
 
˚C
230-280
最佳加工温度MeltTemp.Optimum
 
 
˚C
260
模具温度
MoldTemp.Range
 
 
˚C
50~70
干燥温度DryTemp.
 
 
˚C
100~130
去湿干燥时间
DehumidifiedDryTime
 
 
hrs
2~5
含水率
MoistureContent
 
 
%
≤0.02
*以上数值是本公司按照实验标准测定的实验数据,仅作参考。
*上述数据未必适用于各种不同的条件,具体使用还请客户自行判断。
*Thesevaluesareourexperimentaldataunderrelevanttestingmethods.Justforreference.
*Customersareresponsbilefordecidingwhethertheinformationlistedinthisdatesheetisappropriateforcustomer'suseunderdifferentconditions.